ASTM A333 Grade 10 Alloy steel pipe

ASTM A333 Grade 10 Alloy steel pipe ASTM A333 Grade 10 Low-Temperature Alloy Steel Pipe ASTM A333 Grade 10 is a grade of ASTM A333 Standard. ASTM A333/A333M-16 Standard Specification for Seamless and Welded Steel Pipe for Low-Temperature Se

ASTM A333 Grade 10 Alloy steel pipe

ASTM A333 Grade 10 Alloy steel pipe

 
ASTM A333 Grade 10 Low-Temperature Alloy Steel Pipe
 
ASTM A333 Grade 10 is a grade of ASTM A333 Standard.ASTM A333/A333M-16  Standard Specification for Seamless and Welded Steel Pipe for Low-Temperature Service and Other Applications with Required Notch Toughness.
 
ASTM A333 Grade 10 Steel Pipe is suitable for -45 ~ -195 ~ C low temperature pressure vessel pipes and seamless steel tubes for low temperature heat exchanger pipes.

 
 
ASTM A333 Grade 10 Alloy Steel Pipe Manufactor
beite steel pipe supply Alloy Steel Pipe for many years, every year sell more than 800 tons of Alloy Steel Pipe.
 
beite steel pipe  has already provided a series of High Pressure Alloy Steel Pipe, including: ASTM A333 Grade 1 Alloy Steel Pipe,ASTM A333 Grade 4 Alloy Steel Pipe,ASTM A333 Grade 6 Alloy Steel Pipe,ASTM A333 Grade 8 Alloy Steel Pipe,ASTM A333 Grade 10 Alloy Steel Pipe.
 
We can customize and innovate the ASTM A333 Grade 10 Low-Temperature Alloy Steel Pipe with advanced technology. Our all ASTM A333 Grade 10 Alloy Steel Pipes are tested in accordance to internationally recognized standards or our own more stringent internal test procedures, which is developed considering the harsh field conditions. Tension test, flattening test, flaring test, hardness test, hydrostatic or nondestructive electric test be made on  specimens. 

 

 

ASTM A333 Grade 10 Alloy Steel Pipe Quick Details
Company Name: beite steel pipe
Country/Region: China
Product Name:ASTM A333 Grade 10 Alloy Steel Pipe
FOB Price: US $1300-2600 / Ton | 1 Ton/Tons (Min. Order)
Port of Shipment:Tianjin,China
Payment:L/C or T/T
Delivery: 7-15 days after payment
Package:Standard export package,suit for all kinds of transport, or as required.
 

 
ASTM A333 Grade 10 Alloy Steel Pipe Dimensional Range & Specification
Outside Diameter:20 – 215mm
Wall thickness:2mm——15mm
Length:6000mm、12000m or specified length as required. 

 

Materials and Manufacture
Manufacture—The pipe shall be made by the seamless or welding process with the addition of no filler metal in the welding operation. 



Heat Treatment:
Normalize by heating to a uniform temperature of not less than 1500°F [815°C] and cool in air or in the cooling chamber of an atmosphere controlled furnace,reheat to a suitable tempering temperature.

For the seamless process only, reheat and control hot working and the temperature of the hot-finishing operation to a finishing temperature range from 1550 to 1750°F [845 to 945°C] and cool in air or in a controlled atmosphere furnace from an initial temperature of not less than 1550°F [845°C].

Seamless pipe of Grades 10 may be heat treated by heating to a uniform temperature of not less than 1500°F [815°C], followed by quenching in liquid and reheating to a suitable tempering temperature

The test pieces shall be gradually and uniformly heated to the prescribed temperature, held at that temperature for a period of time in accordance with Table 1, and then furnace cooled at a temperature not exceeding 600°F [315°C]. Grade 8 shall be cooled at a minimum rate of 300°F [165°C]/h in air or water to a temperature not exceeding 600°F [315°C].



Table 1 Stress Relieving of Test Pieces


Metal Temperature (A , B) Minimum Holding Time,
h/in. [min/mm]
of Thickness
Grades 10
°F °C
1100 600 1 [2.4]
1050 565 2 [4.7]
1000 540 3 [7.1]



Chemical Composition(%) & Physical Properties of ASTM A333 Grade 10 Alloy Steel Pipe


 
ASTM A333 Grade 10 Alloy Steel Pipe Chemical Composition(%)
 
Steel Grade Chemical Composition(%)
C Mn P S Si Ni Cr Cu Al V Nb Mo
Grade 10 ≤0.20 1.15-1.50 ≤0.035 ≤0.015 0.10-0.35 ≤0.25 ≤0.15 ≤0.15 ≤0.06 ≤0.12 ≤0.05 ≤0.05

When Grades 10 are ordered under this specification, supplying an alloy grade that specifically re- quires the addition of any element other than those listed for the ordered grade in Table 1 is not permitted. However, the addition of elements required for the deoxidation of the steel is permitted.


Product Analysis
At the request of the purchaser, an analysis of one billet or two samples of flat-rolled stock from each heat or of two pipes from each lot shall be made by the manufacturer. A lot of pipe shall consist of the following:

 
NPS Designator Length of Pipe in Lot
Under 2 400 or fraction thereof
2 to 6 200 or fraction thereof
Over 6 100 or fraction thereof




Mechanical Properties

Tensile Requirements

/ Grade 10
/ Ksi Mpa
Tensile strength, min  80 550
Yield strength, min 65 450
   Longitudinal Transverse
Elongation in 2 in. or 50 mm, (or 4D), min, %:  
Basic minimum elongation for walls 516 in. [8 mm] and over in thickness, strip tests, and for all small sizes tested in full section 22 .....
When standard round 2-in. or 50-mm gage length or proportionally smaller size test specimen with the gage length equal to 4D (4 times the diameter) is used 16 .....
For strip tests, a deduction for each 132  in. [0.8 mm] decrease in wall thickness below 516 in. [8 mm] from the basic minimum elongation of the following percentage 1.25B .....

Wall Thickness Elongation in 2 in. or 50 mm, min,  %C
Grade 10
in. mm Longi-
tudinal
Trans-
verse
5⁄16 (0.312) 8 22 ....
9⁄32 (0.281) 7.2 21 ....
1⁄4 (0.250) 6.4 20 ....
7⁄32 (0.219) 5.6 18 ....
3⁄16 (0.188) 4.8 17 ....
5⁄32 (0.156) 4 16 ....
1⁄8 (0.125) 3.2 15 ....
3⁄32 (0.094) 2.4 13 ....
1⁄16 (0.062) 1.6 12 ....
 

The following table gives the calculated minimum values.
Calculated elongation requirements shall be rounded to the nearest whole number.
 
Note:The preceding table gives the computed minimum elongation values for each 1⁄32in. [0.80mm] decrease in wall thickness. Where the wall thickness lies between two values shown above, the minimum elongation value is determined by the following equation:

Grade Direction of Test Equation
Longitudinal E = 40+ 9.50 [= 1.56+ 9.50]
where:
E  =  elongation in 2 in. or 50 mm, in %,  and   t   =  actual thickness of specimen, in. [mm].


Impact Requirements
For Grades 10 the notched-bar impact properties of each set of three impact specimens, including specimens for the welded joint in welded pipe with wall thicknesses of 0.120 in. [3 mm] and larger, when tested at temperatures in conformance with 14.1 shall be not less than the values prescribed in Table . 
 
TABLE  Impact Requirements for Grades 1

Size of Specimen, mm Minimum Average Notched Bar Impact Value of Each Set of Three SpecimensA Minimum Notched Bar Impact Value of One Specimen Only of a SetA
ft·lbf J ft·lbf J
10 by 10 13 18 10 14
10 by 7.5 10 14 8 11
10 by 6.67 9 12 7 9
10 by 5 7 9 5 7
10 by 3.33 5 7 3 4
10 by 2.5 4 5 3 4





Workmanship, Finish and Appearance
The pipe manufacturer shall explore a sufficient num- ber of visual surface imperfections to provide reasonable assurance that they have been properly evaluated with respect to depth. Exploration of all surface imperfections is not required.
 
 
Surface imperfections that penetrate more than 12½ % of the nominal wall thickness or encroach on the minimum wall thickness shall be considered defects. 
 
 
 


Mechanical Testing
SamplingFor mechanical testing
Transverse or Longitudinal Tensile Test and Flattening Test
Hydrostatic Test—Each length of pipe shall be sub- jected to the hydrostatic test.
 
Impact Test
 
 
Impact Tests (Welded Pipe)—On welded pipe


Impact Test
Except when the size of the finished pipe is insufficient to permit obtaining subsize impact specimens, all material furnished to this specification and marked in accordance shall be tested for impact resistance at the minimum temperature for the respective grades as shown in Table .

ASTM A333 Grade 1 Alloy Steel Pipe Impact temperature
Steel Grade Impact temperature
Grade 10 -75 -60





Hydrostatic or Nondestructive Electric Test
 


Product Marking
in addition to the marking prescribed in Specification A 999/A 999M, the mark- ing shall include whether hot finished, cold drawn, seamless or welded, the schedule number and the letters “LT” followed by the temperature at which the impact tests were made, except when a lower test temperature is required because of reduced specimen size, in which case, the higher impact test tempera- ture applicable to a full-size specimen should be marked.


 
ASTM A333 Grade 10 Alloy Steel Pipe Packaging & Delivery


 

 
Types of Packaging:
- Bundles (hexagonal)
- Wooden Boxes
- Crates (steel/wooden)
- Special crates for U-Bend tubes with each radius separated
- Our ASTM A333 Grade 10 Alloy Steel Pipe packing can meet any needs of the customers.
 
 
Delivery: 7-15 days after payment


 

Contact:Lucky

whatapp: +8615003211561

E-mail:jinxiaolong0221@gmail.com


Product key description, this is a very good product description, detailing our product use, product characteristics

Mail consultation
Please feel free to give your inquiry in the form below.We will reply you in 24 hours.